| CHEMISTRY | X-SBR LATEX |
| SOLID CONTENT | 49-50 |
| VISCOSITY | 200-900 |
| MFFT | >0 |
| PH | 7.5-8.5 |
| FILM HARDNESS | very soft |
| Chemistry | X-SBR LATEX |
| viscosity | 150-500 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 10 |
| Film Hardness | Medium to Soft |
softer than PAYTEX M15T good filler load ability excellent water resistant , dipping and back coating technic
| Chemistry | X-NBR LATEX |
| viscosity | 30-130 |
| Solid Content | 40-41 |
| PH | 7-8 |
| MFFT | >0 |
| Film Hardness | SOFT |
oil resistant industrial nitrile gloves
| Chemistry | X-SBR LATEX |
| viscosity | 100-300 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 45 |
| Film Hardness | Hard |
dipping of non woven and back Coating of carpet
| Chemistry | X-SBR LATEX |
| viscosity | 250-650 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness | Soft |
high filler/polymer ratio , harder than PAYTEX NL25 , excellent adhesion
| Chemistry | SBR LATEX |
| viscosity | < 200 |
| Solid Content | 40 |
| PH | 10 |
| MFFT | 0 < |
| Film Hardness | very Soft |
for natural and nitrile latex compounding
| Chemistry | X-SBR LATEX |
| viscosity | 500-2500 |
| Solid Content | 48-50 |
| PH | 4-5 |
| MFFT | >0 |
| Film Hardness | very Soft |
for modification cationic emulsion bitumen
| Chemistry | Polyacrylate |
| viscosity | 40-120 |
| Solid Content | 25-26 |
| PH | 5.5-6.5 |
| MFFT | - |
| Film Hardness | - |
for neutral and alkaline dispersion in water , specially for metal oxide and carbonate minerals
| Chemistry | X-SBR LATEX |
| viscosity | 100-300 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 58 |
| Film Hardness | Hard |
heat forming textiles , excellent water resistant , dipping and back coating technic
| Chemistry | X-SBA LATEX |
| viscosity | 300-600 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness |
high adhesion to polyethylene and polypropylene films , tacky dry film
| Chemistry | X-SBR LATEX |
| viscosity | 200-900 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness | very soft |
for compounding with natural latex and nitrile latex
Ürünlerimizin çevreye ciddi bir hasarı yoktur
bizim malzeme konteyner taşıma sorunu yok 5 ila 35C˚ arasında donma ve güneş ışığından koruyun
Bu ürünün son kullanma tarihi: en az altı ay, Uygun kapalı depoda saklayın.
Maddelerin ve karışımların sınıflandırılması, etiketlenmesi ve ambalajlanması, 67/548 / EEC ve 1999/45 / EC sayılı Direktiflerin değiştirilmesi ve yürürlükten kaldırılması ile Yönetmelikte değişiklik yapılması hakkında 16 Aralık 2008 tarih ve 1272/2008 sayılı AVRUPA PARLAMENTOSU VE KONSEYİ TÜZÜĞÜ (AT) (EC) 1907/2006 No