| CHEMISTRY | X-SBR LATEX |
| SOLID CONTENT | 49-50 |
| VISCOSITY | 100-300 |
| MFFT | 45 |
| PH | 7.5-8.5 |
| FILM HARDNESS | Hard |
| Chemistry | X-NBR LATEX |
| viscosity | 30-130 |
| Solid Content | 41-43 |
| PH | 8-10 |
| MFFT | >0 |
| Film Hardness |
oil resistant industrial nitrile gloves
| Chemistry | X-SBR LATEX |
| viscosity | 200-900 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness | very soft |
for compounding with natural latex and nitrile latex
| Chemistry | X-SBR LATEX |
| viscosity | 100-300 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 68 |
| Film Hardness | Hard |
heat forming textiles , excellent water resistant , dipping and back coating technic
| Chemistry | X-SBR LATEX |
| viscosity | 100-300 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 45 |
| Film Hardness | Hard |
dipping of non woven and back Coating of carpet
| Chemistry | SBR LATEX |
| viscosity | < 200 |
| Solid Content | 40 |
| PH | 10 |
| MFFT | 0 < |
| Film Hardness | very Soft |
for natural and nitrile latex compounding
| Chemistry | X-SBR LATEX |
| viscosity | 100-300 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 45 |
| Film Hardness | Hard |
dipping of non woven and back Coating of carpet
| Chemistry | Polyacrylate |
| viscosity | 40-120 |
| Solid Content | 25-26 |
| PH | 5.5-6.5 |
| MFFT | - |
| Film Hardness | - |
for neutral and alkaline dispersion in water , specially for metal oxide and carbonate minerals
| Chemistry | X-SBR LATEX |
| viscosity | 100-300 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 58 |
| Film Hardness | Hard |
heat forming textiles , excellent water resistant , dipping and back coating technic
| Chemistry | X-SBR LATEX |
| viscosity | 200-900 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 0 |
| Film Hardness | Very Soft |
high filler load ability, excellent water resistant , dipping and back coating technic
| Chemistry | X-SBA LATEX |
| viscosity | 100-500 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness |
high adhesion to polyethylene and polypropylene films , tacky dry film
Ürünlerimizin çevreye ciddi bir hasarı yoktur
bizim malzeme konteyner taşıma sorunu yok 5 ila 35C˚ arasında donma ve güneş ışığından koruyun
Bu ürünün son kullanma tarihi: en az altı ay, Uygun kapalı depoda saklayın.
Maddelerin ve karışımların sınıflandırılması, etiketlenmesi ve ambalajlanması, 67/548 / EEC ve 1999/45 / EC sayılı Direktiflerin değiştirilmesi ve yürürlükten kaldırılması ile Yönetmelikte değişiklik yapılması hakkında 16 Aralık 2008 tarih ve 1272/2008 sayılı AVRUPA PARLAMENTOSU VE KONSEYİ TÜZÜĞÜ (AT) (EC) 1907/2006 No