| CHEMISTRY | SBR LATEX |
| SOLID CONTENT | 40 |
| VISCOSITY | < 200 |
| MFFT | 0 < |
| PH | 10 |
| FILM HARDNESS | very Soft |
| Chemistry | X-NBR LATEX |
| viscosity | 30-130 |
| Solid Content | 40-41 |
| PH | 7-8 |
| MFFT | >0 |
| Film Hardness |
oil resistant industrial nitrile gloves
| Chemistry | X-SBR LATEX |
| viscosity | 100-400 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 58 |
| Film Hardness | Hard |
heat forming textiles , excellent water resistant , dipping and back coating technic
| Chemistry | X-SBR LATEX |
| viscosity | 200-900 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | 0 |
| Film Hardness | Very Soft |
high filler load ability, excellent water resistant , dipping and back coating technic
| Chemistry | X-SBR LATEX |
| viscosity | 50-300 |
| Solid Content | 49-50 |
| PH | 6.5-7.5 |
| MFFT | >0 |
| Film Hardness | soft |
high filer load ability,highly flexible and good adhesion to fibers of artificial grass
| Chemistry | Polyacrylate |
| viscosity | 40-120 |
| Solid Content | 25-26 |
| PH | 5.5-6.5 |
| MFFT | - |
| Film Hardness | - |
for neutral and alkaline dispersion in water , specially for metal oxide and carbonate minerals
| Chemistry | X-SBA LATEX |
| viscosity | 100-500 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness |
high adhesion to polyethylene and polypropylene films , tacky dry film
| Chemistry | X-SBR LATEX |
| viscosity | 50-300 |
| Solid Content | 49-50 |
| PH | 6-7 |
| MFFT | > 15 |
| Film Hardness | medium to hard |
high filer load ability,low viscosity compounding,excellent adhesion for secondary back coating for wall to wall carpet
| Chemistry | X-SBR LATEX |
| viscosity | 200-900 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness | very soft |
for compounding with natural latex and nitrile latex
| Chemistry | X-SBR LATEX |
| viscosity | 200-500 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness | Soft |
Back Coating,high filler load ability excellent water resistant , dipping and back coating technic
| Chemistry | X-SBR LATEX |
| viscosity | 200-900 |
| Solid Content | 49-50 |
| PH | 7.5-8.5 |
| MFFT | >0 |
| Film Hardness | very Soft |
modification of anionic emulsion bitumen.crack resistance in low temperature and flow resistance in high temperature
محصولات ما آسیب جدی به محیط زیست وارد نمی کنند
مواد ما هیچ مشکلی در برخورد با ظروف ندارد آن را از یخ زدگی و نور خورشید بین 5 تا 35 درجه سانتیگراد نگه دارید
تاریخ انقضاء این محصول: حداقل شش ماه ، آن را در انبار داخلی مناسب نگه دارید.
مقرره (EC) شماره 1272/2008 مجله اروپایی و شورا در تاریخ 16 دسامبر 2008 در مورد طبقه بندی ، برچسب زدن و بسته بندی مواد و مخلوط ها ، اصلاح و لغو دستورالعمل های 67/548 / ΕΟΚ و 1999/45 / EC و اصلاح آیین نامه (EC) شماره 1907/2006